  • 1.4418(X4CrNiMo16-5-1,AISI S165M,Z6CND16-05-01) Forged Forging Stainless Steel Pump Shafts Spindles

Details

 aisi_4317_17crnimo6_18crnimo_7_6_1_6587_forged_forging_steel_pump_shafts.jpg

We are professional 1.4418(X4CrNiMo16-5-1,Z6CND16-05-01,AISI S165M,X4CRNIMO16.5.1,X 4 Cr Ni Mo 16-5-1,Z 6 CND 16-05-01) Forged Forging stainless steel CNC machining Turning Milling Grinding Turned machined Submersible Mixer Pump Splined spline Shafts shipping boat ship Propeller shafting Spindles from china

 

1.4418
X4CrNiMo16-5-1

C

Si

Mn

P

S

Cr

Mo

Ni

V

min.

 

 

 

 

 

15,0

0,8

4,0

   

max.

0,06

0,7

1,5

0,04

0,02

17,0

1,5

6,0

   

1.4418(X4CrNiMo16-5-1,Z6CND16-05-01,AISI S165M,X4CRNIMO16.5.1,X 4 Cr Ni Mo 16-5-1,Z 6 CND 16-05-01) Stainless is a martensitic stainless steel specially designed for those applications requiring high mechanical properties combined with improved corrosion resistance relative to traditional martensitic steels.

1.4418(X4CrNiMo16-5-1,Z6CND16-05-01,AISI S165M,X4CRNIMO16.5.1,X 4 Cr Ni Mo 16-5-1,Z 6 CND 16-05-01) Stainless is also offered as an enhanced machining variant, 1.4418  stainless, which obtains an enhanced machinability characteristic through controlled addition of sulfur without degrading strength or corrosion resistance. 1.4418 EM Stainless contains differentiated micro constituents for easier machining production.

Corrosion Resistance

This alloy shows good corrosion resistance to mild atmospheres, both in annealed and heat-treated conditions. It resists corrosion in many industrial and domestic environments as well as potable and mine waters.

For optimum corrosion resistance, surfaces must be free of scale, lubricants, foreign particles, and coatings applied for drawing and heading. After fabrication of parts, cleaning and/or passivation should be considered.

Annealing

This alloy is typically annealed at 1112°F - 1200°F (600°C - 650°C), followed by slow cooling in air. Heat uniformly to the selected temperature.

Hardening

Heat to 1740°F - 1920°F (950°C - 1050°C), followed by oil quench. Small sections can be hardening by air cool.

Tempering

 

QT900 properties are achieved by tempering at 1025°F - 1145°F (550°C - 620°C) for 8 hours followed by oil or air cool. Alternately, material may be treated using two cycles, 4 hours each followed by oil or air cool. This alloy may suffer temper embrittlement if tempered at 785°F - 1022°F (450°C - 550°C), or slow cool at this temperature range.

Forging & Heat Treatment Equipment List

  • Name & Description

    Forging Handling Capacities 

      Quantity

    3150 Tons Free Forging Hydraulic Press

    Max. Single Forging in 28 Tons

    5000mm Diameter Rolling Forging Machine  

    Max. Single Forging in 16 Tons

    1

    8 Tons Free Forging Hummer

    Max. Single Forging in 7.5 Tons 

    1

    6 Tons Free Forging Hummer

    Max. Single Forging in 5.5 Tons 

    1

    Tons Free Forging Hummer

    Max. Single Forging in 4.5 Tons 

    1

    60 Tons Forging Handling Operator  

    Max. Single Forging in 45 Tons  

    1

    10 Tons Forging Handling Operator 

    Max. Single Forging in 7.5 Tons   

    1

    80 Tons Crane

    Max. Single Ingot in 80 Tons 

    60/30 Tons Crane

    Max. Single Ingot in 60 Tons 

    1

    30/10 Tons Crane

    30/10 Tons 

    4

    Trolley Heat Furnace

    5000*1500*1200 mm  

    3

    Trolley Heat Furnace

    8000*2000*1600 mm  

    Trolley Heat Furnace

    6500*1500*1200 mm  

    3

    Vertical Heat Furnace

    Ø2500*10000 mm

    2

      Total Forging Equipment Quantity

    24      

Hits:  UpdateTime:2016年12月25日 10:33:41  【Printing】  【Close