 We are professional 17CrNi6-6 17CrNi66 17 CrNi 6-6 17CrNi6.6 Forged forging Steel Round Bars Rods Square rectangular rectangle Flat Hex Bars,17CrNi6-6 17CrNi66 17 CrNi 6-6 17CrNi6.6 Forged Forging Steel Hollow Bars Forged Forging Sleeves Bushes Bushing Pipes Piping tube tubings barrels Casing Cases Shells cylinders hubs housings,17CrNi6-6 17CrNi66 17 CrNi 6-6 17CrNi6.6 Seamless Rolled Steel Rings,17CrNi6-6 17CrNi66 17 CrNi 6-6 17CrNi6.6 Forged Forging Steel rings,17CrNi6-6 17CrNi66 17 CrNi 6-6 17CrNi6.6 Forged Forging Steel Blocks Discs Disks Plates,17CrNi6-6 17CrNi66 17 CrNi 6-6 17CrNi6.6 Forged Forging Steel Gear Shafts Pinion Shafts Spindles bevel gears crown wheels crankshafts,and other 17CrNi6-6 17CrNi66 17 CrNi 6-6 17CrNi6.6 forged forging parts Forged Products forged forging pieces forged forging steel components materials pieces products from china


Chemical composition %   of   steel   17CrNi6-6    EN 10084-2008
Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser, other than for the purpose of finishing the heat.
Steels with improved machinability as a result of the addition of lead or higher sulfur contents, depending on the manufacturing process up to around 0.1 % S, may be supplied on request. In this case, the upper limit of the manganese content may be increased by 0.15 %
C Si Mn Ni P S Cr
0.14 - 0.2 max   0.4 0.5 - 0.9 1.4 - 1.7 max   0.025 max   0.035 1.4 - 1.7


Mechanical properties of   steel   17CrNi6-6 

Nominal thickness (mm):   to 16
Rm - Tensile strength (MPa) hardening and tempering at 200 1200
Rm - Tensile strength (MPa) (+AC) 600


Z - Reduction in cross section on fracture (%) 57-62


  Brinell hardness   (HBW):   (+S) 255
  Brinell hardness   (HBW):   (+A) 229
  Brinell hardness   (HBW):   (+TH) 175 - 229
  Brinell hardness   (HBW):   (+FP) 156 - 207